A7 TIG Orbital System 150© Kemppi Oy 2016 1615

OPERATING MANUAL

Problem Possible solution

Arcing within the

weld head (see

Maintenance section)

Contaminated eroded or improper length tungsten electrode.

• Improperly cleaned tube surface or poor contact between collets

and tube may cause arcing between tube/pipe collets.

• Metal debris on the inside surface of the weld head.

• Arc-starting amperage too low.

High frequency but no

weld current

Check for broken electrode or ground cable in the weld head, handle,

or in the cable.

Defects in butt welds

Lack of penetration

with work piece in

5G (horizontal) or 2G

(vertical) positions

• Insucient current

• Rotation speed too high

• Contaminated gas, insucient gas or wrong gas

• Arc gap too great, wrong tungsten tip conguration or

Contaminated/worn tungsten electrode

• Gas ow too high

• Arc not on the joint

• Tube wall dimensional variation

• End of tube not square

• Too much gas on I.D. or no I.D. purge

• Tubes not cleaned

ID location • Increase rotation delay or increase Level 1 amps

• Increase weld current or decrease weld head speed

• Use next weld level 2 to increase amps

• Downslope starting too soon; increase time at last level or use Start

position to initiate downslope.

Concavity (suck-

back) or excessive

penetration

• All ID locations

• Weld current too high

• Rotation speed too low

• Tubes not tightly butted together

• Tubes ends not square

• ID purge gas pressure too high; create larger gas exit hole

Over-penetration General

Most common through the 12 o’clock position in 5G (tube horizontal)

welding

• Increase rotation speed

• Decrease weld current

• Contaminated or improper gas

• Gas ow too high

• Tungsten arc gap may have changed or tungsten conguration has

changed

• Weld head not in calibration

• Tubes not tightly butted

• Tube ends not square

ID location

• Rotation delay period too long, too much weld current or

• Rotation too low

• Increase speed or decrease current

• Current too high in weld level or may need to change to another

level with reduction in current

• Increase rotation delay or increase Level 1 amps

• Increase weld current or decrease Head speed

• Use next weld Level 2 to increase amps

• Downslope starting too soon; increase time at last level or use Start

position to initiate downslope

Porosity or improper

gas coverage

• Contaminated gas or improper gas

• Oil, dirt or other contaminant on tube ID/OD.

Hole in gas line aspirating air.

• Pre-purge/postpurge time too short

• Poor welding tube alloy

• Gas ow rate ID or OD too low

Missbrauch melden von Frage und/oder Antwort

Libble nimmt den Missbrauch seiner Dienste sehr ernst. Wir setzen uns dafür ein, derartige Missbrauchsfälle gemäß den Gesetzen Ihres Heimatlandes zu behandeln. Wenn Sie eine Meldung übermitteln, überprüfen wir Ihre Informationen und ergreifen entsprechende Maßnahmen. Wir melden uns nur dann wieder bei Ihnen, wenn wir weitere Einzelheiten wissen müssen oder weitere Informationen für Sie haben.

Art des Missbrauchs:

Forenregeln

Um zu sinnvolle Fragen zu kommen halten Sie sich bitte an folgende Spielregeln:

Lesen Sie zuerst die Anleitung;
Schauen Sie nach, ob die Frage bereits gestellt wurde;
Stellen Sie die Frage so deutlich wie nur einigermaßen möglich;
Erwähnen Sie was Sie bereits versucht haben um das Problem zu lösen;
Ist Ihr Problem von einem Besucher gelöst dann lassen Sie ihn / sie wissen in diesem Forum;
Falls Sie reagieren möchten, so verwenden Sie bitte das Antworten- Formular;
Da ihre Frage für alle Besucher sichtbar ist, sollten Sie lieber keine persönliche Daten erwähnen.

Kemppi A7 TIG Orbital System 150 Seite 43

Brauchen Sie Hilfe? Stellen Sie Ihre Frage.

Missbrauch melden von Frage und/oder Antwort

Art des Missbrauchs:

Forenregeln

Neu registrieren

Das Handbuch wird per E-Mail gesendet. Überprüfen Sie ihre E-Mail.

Ihre Frage wurde zu diesem Forum hinzugefügt

Info